Wastewater Treatment Plant Containment Area Protection
The Problem The original coating had failed following an incident when a valve had leaked and 3 quarts of 95% sulfuric acid had spilled onto the containment area lining. As…
Read more
The Problem The original coating had failed following an incident when a valve had leaked and 3 quarts of 95% sulfuric acid had spilled onto the containment area lining. As…
Read more
The Problem The EPA was about to fine this automotive engine manufacturer for the condition of their secondary containment. One of the issues was that if this tank leaked, the…
Read more
The Problem This steel mill had a severely corroded secondary containment area caused by hydrochloric acid at elevated temperatures continuously hitting their trench. USI was called in by an engineering…
Read more
The Problem This steel mill had a severely corroded secondary containment area caused by hydrochloric acid at elevated temperatures continuously hitting their trench. USI was called in by an engineering…
Read more
The Problem This steel mill had a severely corroded secondary containment area caused by hydrochloric acid at elevated temperatures continuously hitting their trench. USI was called in by an engineering…
Read more
The Problem At this power station, there were many sulfuric acid spillages from the pumps and tanks operated by the power company. The sulfuric acid had severely eroded the concrete…
Read more
The Problem A mid-west municipal power plant required a recommendation for the right coating and surface preparation procedures to assure a long-time performance for their bleach house secondary containment (12%…
Read more
The Problem The EPA was about to fine this automotive engine manufacturer for the condition of their secondary containment. One of the issues was that the wall rebar was exposed…
Read more
The Problem The EPA was about to fine this automotive engine manufacturer for the condition of their secondary containment. One of the issues was that if this tank leaked, the…
Read more